CAD/CAM Discs
Multi-layered zirconia Katana disc by Kuraray Noritake
KATANA Zirconia YML
Highly aesthetic one-for-all option.Translucency
| Enamel: | Body 1: | Body 2, 3: |
| 49% | 47% | 45% |
Flexural Strength
| Enamel: | Body 1: | Body 2, 3: |
| 750 MPa | 1,000 MPa | 1,100 MPa |
Application range
- Monolithic Crowns
- Monolithic Bridges
- Cut-back frameworks
Sintering Schedule
High speed sintering. Up to 54-minutes.
CZR staining and glazing compatible.
KATANA Zirconia STML
Excellent choice for posterior crowns and bridges.Translucency
| 49% |
Flexural Strength
| 748 MPa |
Application range
- Monolithic Crowns
- Monolithic Bridges (up to 3-unit)
- Cut-back frameworks (up to 3-unit)
Sintering Schedule
High speed sintering. Up to 54-minutes.
CZR staining and glazing compatible.
KATANA Zirconia HTML PLUS
The solution for complex restorations and frameworks.Translucency
| 45% |
Flexural Strength
| 1,150 MPa |
Application range
- Monolithic Crowns
- Monolithic Bridges
- Cut-back frameworks
- Frameworks
Sintering Schedule
High speed sintering. Up to 54-minutes.
CZR staining and glazing compatible.
KATANA Zirconia UTML
For true-to-life anterior restorations.Translucency
| 51% |
Flexural Strength
| 557 MPa |
Application range
- Monolithic Crowns (Anterior)
- Monolithic Bridges (Anterior, up to 3-unit)
- Cut-back frameworks (Anterior, up to 3-unit)
Sintering Schedule
High speed sintering. Up to 54-minutes.
CZR staining and glazing compatible.
KATANA Zirconia HT
For porcelain fused zirconia restorations.Translucency
| 45% |
Flexural Strength
| 1,125 MPa |
Application range
- Frameworks
- Anterior FCZ crowns, FCZ bridges
- Inlays, onlays and veneers
Sintering Schedule
90-minutes and 7 hours.
CZR Porcelains